Description:
Tin cure silicone rubber for plaster/gypsum mold making with two parts, part A is the silicone rubber base, part B is the condensation curing agent. SE-530#&SE-535# is in the harness of 35 & 40 shore A, then the application of these would be used to make mould of the products in larger size, such as the plaster gypsum window decoration, GRC/GRFC products, furniture, roman column mold making, etc.
Its mixing ratio is 100:3, and generally 3% free catalyst would be offered. But in the same mixing ratio, the higher the temperature is, the faster the silicone rubber would be cured. So, please add the catalyst accordingly.

Characteristics:
1. Suitable for both pouring molding and brushing molding
2. Strong tear strength and tensile strength
3. Easily release air to avoid bubbles
4. excellent non-stick effect
5. Various hardness from 5 to 40 shore A
6. Excellent flexibility, easy to demould.
7. High temperature resistance, high duplication times and repeated use
8. Good cut-growth resistance

Application:
Tin cure silicone for mold making, which with good tensile strength as well as high duplication times ,so it is perfect for making mold in statue and figures industries ,such as Stone figurine ,ceramic statues,polyurethane statuary, ceramic statues,polyurethane animals,Buddha, plaster ceiling,gypsum artificial stone, GRC home decorations etc.while,it also application for making mold for Resin and poly resin crafts, Lighting ornaments, candles crafts, statue Buddha, relief, artifacts copied, Animals and plants sculpture.

Datesheet:

Model NO·	SE-530#	SE-535#
Mixing Ratio (by weight)	100:3	100:3
Appearance/Color	White	White
Hardness (Shore A)	30±2	35±2
Mixed viscosity (mPa·s)	20000±500	21000±500
Working Time(at23℃,MINS)	30~40	30~40
Curing Time (at 23℃, HRS)	4~5	4~5
Tensile strength, Mpa	≥4.0	≥4.0
Tear strength, KN/m	≥29.5	≥26.8
Shrinkage, %	<0.2	<0.2
Elongation at break, %	≥420	≥400

Using instructions:
Step 1: prepare the original molds

Step 2: Vacuum pumping
Without exception, this step takes less than 10 minutes.(normally is 5munites) Otherwise, it will cause cross linking reaction, and no more further steps will be available.

Step 3: Pouring casting or Brushing operation

Step 4:Demoulding:
After 35 hours later, can demould the silicone mold, it's will be better for molf to demould after 24 hours.
Notes:The curing temperature and curing time can be adjustable according to the operation conditions.